BWG18 Hot Dipped Galvanized Iron Soft Binding Wire Low Carbon Q195 Q235
- TIANRUI
- Tianjin,China
- 7-25days
- 2000 Ton/Tons per Month
Hot Dipped Galvanized Wire
Factory direct hot dipped galvanized iron wire for binding wire
Place of Origin:
Tianjin, China (Mainland)
Material:
Q195,Q235,SAE1006/1008 etc.
zinc coating:20-280g/m2,
Tensile Strength:350-550Mpa
Coil weight:1kg-1000kgs/coil
Wire Diameter:0.35-4.2mm
-
Main specification
|
Nominal wire diameter mm
|
Minimum tensile strength Mpa
|
Minimum stress at 1%
elongation Mpa
|
Minimum stress elongation(L=200mm) %
|
NO.of torsion twists(time/360°)
|
|
1.25-2.25
|
1310
|
1170
|
4
|
18
|
|
2.26-3.00
|
1310
|
1170
|
4
|
18
|
|
3.01-3.8
|
1310
|
1170
|
4
|
18
|
|
Nominal wire diameter mm
|
The mass of zinc coating g/m2 Minimum
|
Minimum No.of one Minute dips
|
Mandrel Dia (Times of steel wire Dia)
|
No. of warpping turns
|
|
1.25-1.5
|
185
|
2
|
1-2
|
8
|
|
1.51-1.75
|
200
|
2
|
||
|
1.76-2.25
|
215
|
3
|
||
|
2.26-2.75
|
230
|
3
|
||
|
2.76-3.50
|
245
|
4
|
1-3
|
|
|
3.51-3.80
|
260
|
4
|
1-3
|
2.Packaging Details
Bound with steel strips and wrapped with plastic-lined woven bag, or any other particular requirements from customers.
3.Advantages:
1.Smooth and shining surface.
2.Overcome disadvantage of regular zinc layer thickness lack, our zinc layer thickness is far more than country standard requirement to ensure products service life.
3.Zinc coated layer has good adhesiveness with steel wire.
4.Better corrosion prevention ability and durable strength.
5.Steel core satisfy IEC standard requirement for electrical resistivity.
6.Choose good high quality high carbon steel bar as row materials and draw steel core by advanced technology,make sure product's stable and reliable mechanical property .